- Samsung Cheil Industries Starex® LX-0987EXS ABS, Unreinforced Metallic-Look
Samsung Cheil Industries Starex® LX-0987EXS ABS, Unreinforced Metallic-Look
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® LX-0987EXS ABS, Unreinforced Metallic-Look.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Temperature 23.0 °C |
0.050 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 10.0 kg, Temperature 220 °C |
12 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength at Break | 34.3 MPa | 4970 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 46.1 MPa | 6680 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 14 % | 14 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 64.7 MPa | 9380 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.26 J/cm @Thickness 6.35 mm |
4.22 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.35 J/cm @Thickness 3.17 mm |
4.41 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | B/50; ISO R306 |
| 102 °C | 216 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 BT Polyamide 6
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N220 Filler
- Lucite International Diakon® LG156 Acrylic Bead Polymer, High Transparency
- Materion Beryllium Nickel Strip - Alloy 360 1/4 Hard, 2.5 hr at 950°F
- Techmer ES HiFill® PP GF10 10% Glass Filled
- Formosa Plastics Formolon® APW Compound
- Dow Corning SILASTIC® Q4-2857 SILICONE RUBBER
- DSM Akulon® K222-KWGV4 Nylon 6-20% Glass Reinforced (European and Asian Grade) (Dry)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.25 PHR Zinc Stearate
- DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved