Inno-Comp INNOPOL® CS 2-3110 TO BU 10% Talc Filled Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-3110 TO BU 10% Talc Filled Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-3110 TO BU is a 10% talc-filled, black colored and UV stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-3110 TO BU is developed for producing injection molded automotive components, where the required properties are the good stiffness and excellent impact resistance.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 1183 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.25 GPa | 181 ksi | ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 250 °C | 374 - 482 °F | Injection |
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | Injection |
| Front Barrel Temperature | 190 - 250 °C | 374 - 482 °F | Injection |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | Injection |
| Mold Temperature | 10.0 - 50.0 °C | 50.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP/PE TD 10 | ISO 1043 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® OQ3420 PC (Europe-Africa-Middle East)
- Karina 57/200-D-AT-IS-SD Clear PVC Compound
- Techmer ES Electrafil® DB-1200/S/7/FR ABS, 7% Stainless Steel Fiber Reinforced (dry blend), Flame Retardant
- Shin-Etsu Silicones KE-1052A/B Silicone, Gel RTV
- Shakespeare NX-310 diameter 0.4 mm Nylon 66 Monofilament
- SCG Chemicals EL-Proâ„¢ P700J Polypropylene Injection Molding
- Zotefoams Plastazote® LD24FMSV Low Density Polyethylene Foam, Flame Retarded
- Dow Corning MOLYKOTE® G-0101
- Esstech V-117-1140 Barium Borosilicate Glass
- Cadi 10 MOLD-MOR™
Copyright © lookpolymers.com All Rights Reserved