- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- LG Chemical AF-348 ABS, Flame Retardant, Heat Resistant, Weather Resistant
LG Chemical AF-348 ABS, Flame Retardant, Heat Resistant, Weather Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical AF-348 ABS, Flame Retardant, Heat Resistant, Weather Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Melt Index of Compound | 50.85 g/10 min @Load 10.0 kg, Temperature 220 °C |
50.85 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 25 % | 25 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 80 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Annealed, 80°C, 4 hours; ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Annealed, 80°C, 4 hours; ISO 175 |
| Vicat Softening Point | 93.0 °C | 199 °F | 50 N, 50°C/h; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
|
| V-2 @Thickness 2.50 mm |
V-2 @Thickness 0.0984 in |
||
| V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
IEC 250 |
| 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
IEC 250 | |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 75.0 - 80.0 °C | 167 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R7831A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Huntsman IROGRAN® A 92 K 5031 TPU-High Temperature Performance
- Malvern Minerals Sliastic 740 with 33% Novacite® Daper Quartz Filler
- Mitsubishi Iupilon® S2001R 9.5 MFI FDA Compliant Polycarbonate With Release
- Lanxess Durethan® BKV 30 H2.0 EF DUS029 901510 Nylon 6, Glass Fiber Reinforced
- Formosa Plastics Formolene® 6613N Impact Copolymer Polypropylene
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.004 Phosphoric Acid Anodized Aluminum Honeycomb
- DSM Stanyl® TW241B3 PA46-CF15
- ExxonMobil Mobil Permazone Coolant/Antifreeze
- Qualchem Danamid FGFTALX2-5 20 Polyamide 6, 25% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved