Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.40 GPa | 1220 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 6 GF 30 FRG 5 Polyamide 6, 30% Glass Fiber, Halogen Free Flame Retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fiber, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6mm, glow wire at 960°C,.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
NHEP Spectron™ E5469 Nylon 66, 33% Glass Fiber Natural color. E5469 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informat.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
NHEP Spectron™ E6666 Nylon 66, 30% Glass Fiber Natural color. E6666 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 8.44 GPa | 1220 ksi | ASTM D790 |
Plenco 4100 Phenolic, Granular, Injection Molded
(discontinued **) Two-stage Phenolic. PLENCO 04100 is a black two stage, medium heat resistant phenolic molding compound. It has excellent moldability characteristics and molded finish. It is used in appliance and .. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
Plenco Valite 759 Novolac Phenolic, Granular, Injection Molded
(discontinued **) This Valite product has been replaced by Plenco 4759. Data provided by Plenco.VALITE 759 is a black, two stage, medium heat resistant phenolic molding compound. It has excellent molded finish and p.. |
|||
Flexural Modulus | 8.43 GPa | 1220 ksi | 5 mm/min; ISO 178 |
Gromax BFG30-B103N1 Nylon 6 33% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Modulus | 8.41 GPa | 1220 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC LNP* Lubricomp* Lexan_LF1530A compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Flexural Modulus | 8.44 GPa | 1220 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP QFN16 PA 6/10 LNP* LUBRICOMP* QFN16 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 5% MOS2. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 8.41 GPa | 1220 ksi | ISO 178 |
Solvay Technyl® C218V30 30% Glass Filled, Heat Stabilized Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY Description: TECHNYLSTARâ„¢ S 218 V30 is based on a patented high flow polyamide 6 resin (TechnylStar), heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is.. |
|||
Flexural Modulus | 8.41 GPa | 1220 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66 LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | |
SPS Guang Zhou POBUXâ„¢ 3001G30 Flame-retarded/GF30%-PBT Characteristic: Good flame retardance, high mechanical properties, high rigidity, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) .. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East) LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic. |
|||
Flexural Modulus | 8.39 GPa | 1220 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP D351 PC (Asia Pacific) LNP* Thermocomp* D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus,.. |
|||
Flexural Modulus | 8.41 GPa | 1220 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DX06412H PC LNP* THERMOCOMP* DX06412H is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Flexural Modulus | 8.39 GPa | 1220 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU LNP THERMOCOMP* GF006 is a compound based on Polysulfone resin containing 30% Glass Fiber. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | At 2 mm/min; ISO 178 |
Borealis Nepol™ GB402HP 40% Long Glass Fiber Reinforced Polypropylene Nepol GB402HP is a 40% long glass fiber reinforced polypropylene grade, produced using Borealis ` propriety and exclusive, patented Nepol technology intended for injection molding and extrusion. Th.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
Plenco 4327 Phenolic, Granular, Compression Molded PLENCO 04327 is a heat resistant mineral filled phenolic molding compound offering excellent cosmetic characteristics and improved heat resistant properties. PLENCO 04327 is not intended for electri.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
Plenco 6527 Phenolic, Granular, Transfer Molded PLENCO 06527 is a woodflour and mineral filled resole phenolic molding compound.Information supplied by Plenco. |
|||
Flexural Modulus | 8.41 GPa | 1220 ksi | ASTM D790 |
Ecomass® 1700TU96 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications.High Specific GravityTungsten Powder Filled Polyamide (PA) AlloyRigidInformation provided by Technical Po.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600 MZ 315 CP Combination Nylon 66, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
DuPont Performance Polymers Crastin® LW9330 NC010 PBT+SAN
(Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9330 NC010 is a 30% glass fiber reinforced polybutylene terephthalate blend for injection molding. I.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612
(Unverified Data**) 33% Glass Reinforced Polyamide 612 Developed for Electrical and Electronics Applications Zytel FE5382 BK276 is a 33% glass fiber reinforced heat stabilized black polyamide 612 resin developed for el.. |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced for extrusion applications.Data provided by the manufacturer |
|||
Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 623 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |