Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Ashley Polymers
Trade Name Ashlene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nylon 66, 33% glass reinforced for extrusion applications.Data provided by the manufacturer
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ASTM D792
Water Absorption 0.80 %
0.80 %
24 hrs; ASTM D570
Moisture Absorption at Equilibrium 1.7 %
1.7 %
50% RH; ASTM D570
Water Absorption at Saturation 5.4 %
5.4 %
ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Ultimate 180 MPa
26100 psi
ATSM D638
Elongation at Break 10 %
10 %
ASTM D638
Flexural Modulus 8.40 GPa
1220 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm
2.49 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 251 °C
484 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 246 °C
475 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 243 °C
469 °F
ASTM D648