SABIC Innovative Plastics LNP LUBRICOMP QFN16 PA 6/10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP QFN16 PA 6/10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* QFN16 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 5% MOS2. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 162 MPa | 23500 psi | 5 mm/min; ISO 527 |
| 164 MPa | 23800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.94 GPa | 1440 ksi | 1 mm/min; ISO 527 |
| 10.24 GPa | 1485 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 218 MPa | 31600 psi | ISO 178 |
| 228 MPa | 33100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | 2 mm/min; ISO 178 |
| 8.44 GPa | 1220 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.03 J/cm | 1.93 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.18 J/cm | 17.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT UR-50 LGF/000 Natural Polyurethane, Unspecified (PUR, Unspecified)
- LATI Latamid 12 H FE90 PA 12, Heat Stabilized
- Stellar Canada CERAMITE® BKR-S Wear Resistant Castable
- Teknor Apex MF 165-J3 NT Polyvinyl Chloride, Flexible Film
- DSM Stanyl® TS350 PA46 FR(17)
- DuPont™ Surlyn® 1601 Sodium Ionomer Resin for Blown and Cast Film
- DuPont Performance Polymers Sorona® MT3401 NC010 Polytrimethylene Terephthalate (PTT)
- Fainplast Compounds GS 61/R Flexible PVC, Injection Molding for Footwear
- BASF Capron® SEGM35H1 BK-126 15/25% Glass/Mineral-Filled Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved