- Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced
Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber/PTFE Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 - 1.3 % | 0.30 - 1.3 % | ISO 62 |
| Water Absorption at Saturation | 3.5 - 5.5 % | 3.5 - 5.5 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 168 MPa | 24400 psi | ISO 2039-1 |
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 4.50 J/cm² @Temperature -40.0 °C |
21.4 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| 1.10 J/cm² | 5.24 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 140 °C | 284 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- LG Chemical Lucet® N109 Acetal Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP EX03647H PEI
- Techmer ES HiFill® PEEK GF10 10% Glass Filled
- Techmer ES Plastiblend® PA6/ABS 1120 GF15 15% Glass Filled
- Teknor Apex APEX® 4150 Polyvinyl Chloride Compound
- Techmer ES HiFill® TPU/E 0140
- Tra-Con Tra-Bond 2106 Fast Cure, Medium Viscosity Epoxy Adhesive
- DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 50 Gauge
- 3M FVS15S Static Cling Label Materials
Copyright © lookpolymers.com All Rights Reserved