SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 1.1 % @Time 86400 sec |
1.1 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 212 MPa | 30700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
16.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
48.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 238 °C | >= 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- 3M Dyneon™ TF 4103 PTFE 15% Glass Fiber Filled (discontinued **)
- Mateck Cesium Iodide, CsI
- Lubrizol Advanced Materials Pearlbond® 580 Thermoplastic Polyurethane
- Silberline Sparkle Silvet® 790-30-E1
- SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific)
- Teknor Apex Sinpolene MBW1791 Linear Low Density Polyethylene
- Ensinger Tecatron® XP-61 Compression Molded PPS Compound, 25% Fiberglass and Mineral Filled
- 3M Scotch® 825 Pouch Tape
- 3M 21826 Industrial Polyethylene Temporary Surface Protection Tape
Copyright © lookpolymers.com All Rights Reserved