SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* GF006 is a compound based on Polysulfone resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.483 g/cc | 0.05358 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0058 cm/cm @Time 86400 sec |
0.0058 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
| 104 MPa | 15100 psi | ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 8.42 GPa | 1220 ksi | 1 mm/min; ISO 527 |
| 8.82 GPa | 1280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| 156 MPa | 22600 psi | ASTM D790 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| 8.39 GPa | 1220 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.21 J/cm | 7.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 181 °C @Thickness 3.20 mm |
358 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Outokumpu 4742 High Temperature Ferritic Stainless Steel
- MarkeTech Repton 601 Mullite
- IDI Composites C-210 Thermoset Polyester, Sheet
- SABIC Innovative Plastics LNP THERMOCOMP PF004S PA 6
- A. Schulman POLYFORT™ FPP 3717 Talc Filled Homopolymer Polypropylene (39.6% Mineral Content)
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A
- ChevronTexaco Supreme SAE 30 Motor Oil
- Eurotec® Tecopet® PT70 GR30 NL100 XA20 PET, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- BASF Caprolactam Tablets
Copyright © lookpolymers.com All Rights Reserved