Plenco 6527 Phenolic, Granular, Transfer Molded
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Resole, Mineral/Wood Filled |
| Manufacturer | Plenco (Plastics Engineering Company) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 6527 Phenolic, Granular, Transfer Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PLENCO 06527 is a woodflour and mineral filled resole phenolic molding compound.Information supplied by Plenco.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Water Absorption | 0.35 % | 0.35 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00266 cm/cm | 0.00266 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 56 | 56 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 0.77 % | 0.77 % | ASTM D638 |
| Tensile Modulus | 10.6 GPa | 1540 ksi | ASTM D638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Compressive Strength | 143 MPa | 20700 psi | ASTM D695 |
| Izod Impact, Notched | 0.256 J/cm | 0.480 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.243 J/cm² | 1.16 ft-lb/in² | ASTM D256 |
| Impact | 157 | 157 | J/m Drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 188 °C | 370 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ASTM D648 |
| Oxygen Index | 34 % | 34 % | ASTM D2863 |
| Shrinkage | 0.26 % | 0.26 % | 72 hr, 120ºC; ASTM D1299 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.20e+12 ohm-cm | 1.20e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.3 | 6.3 | ASTM D150 |
| Dielectric Strength | 9.30 kV/mm | 236 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.069 | 0.069 | ASTM D150 |
| Arc Resistance | 162 sec | 162 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID® 6 GF 35 LS PA6 reinforced with glass fiber, UV stabilized
- Polykemi AB POLYfill PP CPQ10015 FF Polypropylene, Mineral Reinforced
- MetalTek MTEK 25-12 Cast UNS J93503 Heat Resistant Stainless Steel
- Mitsui APELâ„¢ APL5014DP Cyclo Olefin Copolymer (COC)
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- Dow LDPE 722M Low Density Polyethylene
- DuPont Performance Polymers Neoprene 735A Polychloroprene (discontinued **)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 30 PHR Fumed Silica - Wacker HK N20
Copyright © lookpolymers.com All Rights Reserved