DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
33% Glass Reinforced Polyamide 612 Developed for Electrical and Electronics Applications Zytel FE5382 BK276 is a 33% glass fiber reinforced heat stabilized black polyamide 612 resin developed for electrical bobbins and encapsulation applications.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
1.32 g/cc
0.0477 lb/in³
DAM; ISO 1183
Water Absorption 1.8 %

@Thickness 2.00 mm
1.8 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Moisture Absorption 0.700 %

@Thickness 2.00 mm
0.700 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Viscosity 29770 cP

@Shear Rate 5000 1/s,
Temperature 300 °C
29770 cP

@Shear Rate 5000 1/s,
Temperature 572 °F
ISO 11403-1 -2
35755 cP

@Shear Rate 5000 1/s,
Temperature 290 °C
35755 cP

@Shear Rate 5000 1/s,
Temperature 554 °F
ISO 11403-1 -2
43576 cP

@Shear Rate 5000 1/s,
Temperature 280 °C
43576 cP

@Shear Rate 5000 1/s,
Temperature 536 °F
ISO 11403-1 -2
69238 cP

@Shear Rate 500 1/s,
Temperature 300 °C
69238 cP

@Shear Rate 500 1/s,
Temperature 572 °F
ISO 11403-1 -2
83186 cP

@Shear Rate 500 1/s,
Temperature 290 °C
83186 cP

@Shear Rate 500 1/s,
Temperature 554 °F
ISO 11403-1 -2
101400 cP

@Shear Rate 500 1/s,
Temperature 280 °C
101400 cP

@Shear Rate 500 1/s,
Temperature 536 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
0.0030 cm/cm

@Thickness 3.20 mm
0.0030 in/in

@Thickness 0.126 in
DAM
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
0.010 cm/cm

@Thickness 3.20 mm
0.010 in/in

@Thickness 0.126 in
DAM; ASTM D149
Mechanical Properties Metric English Comments
Tensile Strength at Break 170 MPa
24700 psi
DAM; ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
DAM; ISO 527-1/-2
Tensile Modulus 9.80 GPa
1420 ksi
DAM; ISO 527-1/-2
Flexural Modulus 8.40 GPa
1220 ksi
DAM; ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
DAM; ISO 180/1A
10.0 kJ/m²

@Temperature -40.0 °C
4.76 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 180/1A
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
DAM; ISO 179/1eA
1.00 J/cm²

@Temperature -40.0 °C
4.76 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C
8.33 µin/in-°F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
DAM; ISO 11359-1/-2
Specific Heat Capacity 2.13 J/g-°C
0.509 BTU/lb-°F
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
of melt
Melting Point 218 °C
424 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
421 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
DAM; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
DAM; IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
DAM; IEC 60112
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >PA612-GF33<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification PA612-GF33
PA612-GF33
ISO 1043
Special Characteristics Heat stabilised or stable to heat
UL recognition UL
DAM