Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.96 GPa | 284 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | DIN 53452; ASTM D790 |
Kolon SPESIN® KP513FLBL Multi Reinforced PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Kolon KOCETAL® TF302 Wear Modified Acetal Resin PTFE powder added, improved wear property. Applications: High speed, high load and wear resistant products. Information provided by API-Kolon. |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
LG Chemical LUPOL HG3200SK2 PP+MF20%, High Gloss Description: Injection Molding, PP+MF20%, High GlossApplication: Electrical & Electronic PartsCAS: 9003-07-0 and 7727-43-7Information provided by LG Chemical |
|||
Flexural Modulus | 1.96 GPa @Thickness 6.40 mm |
284 ksi @Thickness 0.252 in |
5mm/min; ASTM D790 |
LG Chemical Lupox® TE5000G PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish, Door Handle)CAS No. 24968-12-5 and 103598-77-2Information provid.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
KKPC Kuhmo HF400 Flame Retarded General Purpose HIPS Key features: Translucent Injection. Common Uses: TV and VCR housing.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-resista.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 5 mm/min; ISO 178 |
Gromax BTE30-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® 1102 PBT+PC (Asia Pacific) Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Asia Pacific) General purpose, UV stabilised Xylex gradeThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Europe-Africa-Middle East) General purpose, UV stabilised Xylex gradeThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xylex X7200MR PC+POLYESTER (Asia Pacific) Mold Release version of X7200This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® BC-0140 H ABS, Unreinforced General Purpose Stiff ABS material for automobile bobbinInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SD-0150AT ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SR-0320BM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SV-0157 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VE-0860SE ABS, Unreinforced FR Flame-retardant ABS material that can be used in the exterior of adaptors, chargers etc.Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP 6450 High Heat Polystyrene Characteristics High impact and modulus Very good flow properties High heat resistance & strength Available in any dark colorProcessing Injection moldingApplications Instrument enclosures Automo.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl EM6100F PPE+PS Automotive interiors. 240F HDT. High impact/good property retention after heat ageing. In blowmolding, better sandability of flash, overblow.This data was supplied by SABIC-IP for the Americas re.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
Tipco Tipcolene® DR 8201 - 20% Talc/Mineral Reinforced, Impact Modified, Polypropylene Copolymer 20% Mineral Reinforced, Impact Modified PP Copolymer BlendApplications: Automotive DashboardsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D-790 |
Axiall 7801 Rigid PVC, Extrusion, White, High Impact Profile Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Flexural Modulus | 1.96 - 5.47 GPa | 284 - 793 ksi | Average value: 2.44 GPa Grade Count:25 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum.. |
|||
Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® EG-0763 ABS, Unreinforced Good chemical resistanceInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP6409 High Gloss Polystyrene Characteristics High gloss in co-extrusion Improved dart impact strength of co-extruded sheets Processing Co-extrusion cap layer Applications Gloss cap layer for refrigerator liner and other formin.. |