A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D792 |
| Melt Flow | 20 - 25 g/10 min @Temperature 230 °C |
20 - 25 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 65 | 65 | ASTM D785 |
| Tensile Strength, Yield | 33.34 MPa | 4836 psi | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 221-55 Thermoplastic Elastomer (discontinued **)
- Permabond F201 Anaerobic Retainer
- Lucent Polymers ABS-45T Acrylonitrile Butadiene Styrene, High Impact
- Solvay Chemicals NOCOLOK® Flux Potassium Fluoroaluminate
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Suprex Clay Filler
- Eurostar Staramide ACF3 PA66, 15% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
- Eurostar Starflam PZ00062E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
- Akro-Plastic Akromid® B3 GF 10 (2829) PA 6 Conditioned, 10% Glass Filled
Copyright © lookpolymers.com All Rights Reserved