Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| 22 g/10 min @Load 10.0 kg, Temperature 250 °C |
22 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.39 J/cm @Thickness 6.35 mm |
10.1 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 6.86 J/cm @Thickness 3.17 mm |
12.9 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C @Thickness 6.40 mm |
264 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 137 °C | 279 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 TF-KV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass ball reinforced
- Microcell Composite Company CELLOMER® 6000 SBS Rubber Pellets
- International Mold Steel DHA-World Die Cast & Forging Steel
- Zircar Zirconia ZYBF-4 Zirconia Bulk Fiber Insulation
- ExxonMobil HDPE HD 7845.30 High Density Polyethylene Resin
- ExxonMobil Varsol™ 40 Non-dearomatized Fluid
- Clariant Renol PCSP0006 Polycarbonate, Laser Markable
- Ensinger Tecast Vekton™ 6PAG Graphite-Filled Cast Nylon 6 (PA6)
- Colorite Polymers 8311 Clear Extrusion Vinyl Compound
- Polyram RamTal PM1027 Acetal, General Purpose
Copyright © lookpolymers.com All Rights Reserved