- Acrylonitrile Butadiene Styrene (ABS), Extruded
- Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.63 J/cm @Thickness 6.35 mm |
6.80 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.31 J/cm @Thickness 3.17 mm |
8.08 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 66, 20% Carbon Fiber Filled
- Hyosung Topilene B240T PP
- Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes
- Samsung Cheil Industries Infino® NH-1014S PC/ABS, Unreinforced FR
- PlastxWorld Veroplas PB3150 Nylon 66
- Total 5202LD HDPE, blow molding
- Cresset Powers Cress-Alon™ A2700 2.7 r.v. Compounding Grade Nylon 6, 50% RH
- Multibase Multi-Flex® TPE A 7606 UV NAT
- PolyOne Edgetek® AT-5GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
- Gouda Vuurvast AK 50 A Dense Refractory Brick
Copyright © lookpolymers.com All Rights Reserved