Gromax BTE30-DN00N1 Nylon 6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BTE30-DN00N1 Nylon 6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ISO 1183 |
| Moisture Absorption | 1.80 % | 1.80 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | 60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | 60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 66.7 MPa | 9670 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 60 % | 60 % | 50 mm/min; ISO 527 |
| Flexural Strength | 78.0 MPa | 11300 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched | >= NB | >= NB | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.620 J/cm² @Temperature -30.0 °C |
2.95 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 2.60 J/cm² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE Z406 Thermoplastic Elastomer, SEBS-based
- Indium Corp. 5N Indium Acetate
- Loxim 340 01HB Nylon 6
- LyondellBasell Lupolen® 1804 H LDPE, Film Grade
- Sinotek Materials Packing Carbon Fiber with Graphite
- Solvay ALKAMULS® S 85 Surfactant
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
- Entec Hypro™ PPC-CC10 Natural Copolymer Polypropylene, 10% Calcium Carbonate Filled
- CIMBAR FlexTalc® 815D Ultrafine Talc for TPO Applications, Densified
- DuPont Performance Polymers Neoprene GNA M2 Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved