Supreme Petrochem SP6409 High Gloss Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer	Supreme Petrochem LTD
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Supreme Petrochem SP6409 High Gloss Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Characteristics High gloss in co-extrusion Improved dart impact strength of co-extruded sheets Processing Co-extrusion cap layer Applications Gloss cap layer for refrigerator liner and other forming applications requiring high toughness Material Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640Information provided by Supreme Petrochem LTD

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Melt Flow	6.0 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 °C	6.0 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	31.4 MPa	4550 psi	50 mm/min; ASTM D638
Elongation at Break	20 %	20 %	50 mm/min; ASTM D638
Flexural Strength	49.0 MPa <br>@Thickness 3.20 mm	7110 psi <br>@Thickness 0.126 in	ASTM D790
Flexural Modulus	1.96 GPa <br>@Thickness 3.20 mm	284 ksi <br>@Thickness 0.126 in	ASTM D790
Izod Impact, Notched	0.400 J/cm <br>@Thickness 3.20 mm	0.749 ft-lb/in <br>@Thickness 0.126 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	78.0 °C	172 °F	ASTM D648
Vicat Softening Point	98.0 °C	208 °F	1kg / 120°C; ASTM D1525
Flammability, UL94	HB <br>@Thickness 1.50 mm	HB <br>@Thickness 0.0591 in

Optical Properties	Metric	English	Comments
Gloss	95 %	95 %	at 60°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 260 °C	356 - 500 °F
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F