- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Samsung Cheil Industries Starex® VE-0860SE ABS, Unreinforced FR
Samsung Cheil Industries Starex® VE-0860SE ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VE-0860SE ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame-retardant ABS material that can be used in the exterior of adaptors, chargers etc.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 29.4 MPa | 4260 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 35.3 MPa | 5120 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 23 % | 23 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.94 GPa | 282 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 54.9 MPa | 7960 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.77 J/cm @Thickness 6.35 mm |
3.31 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.45 J/cm @Thickness 3.17 mm |
4.59 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | B/50; ISO R306 |
| 104 °C | 219 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 - 2.70 mm |
V-0 @Thickness 0.0591 - 0.106 in |
|
| 5VB @Thickness 2.50 - 2.70 mm |
5VB @Thickness 0.0984 - 0.106 in |
Users viewing this material also viewed the following:
- MV Labs RB400 RbCl Rubidium chloride
- Plastcom SLOVAMID 6 NGR PA6, basic type
- Polymax® Maxelast® P3865B TPE, PP Overmold or Standalone use
- Momentive Performance Materials RTV128 Translucent Adhesive Sealant, General Purpose Paste
- LG Chemical Lupox® SG-4405 Surface Gloss PBT, 40% Glass Fiber/Mineral Reinforced, Dimensional Stability
- SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific)
- Techmer ES HiFill® PA4/6 GF25 HS NAT 25% Glass Filled (Dry)
- A. Schulman POLYFORT™ PP 3720
- Colorite Polymers 8588 Non-Phthalate 88 Series Vinyl Compound
- Arlon Thermabond® 99A50X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
Copyright © lookpolymers.com All Rights Reserved