SABIC Innovative Plastics Noryl EM6100F PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl EM6100F PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive interiors. 240F HDT. High impact/good property retention after heat ageing. In blowmolding, better sandability of flash, overblow.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D 792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 40 % | 40 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.960 J/cm @Temperature -40.0 °C |
1.80 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 4.00 J/cm @Temperature 23.0 °C |
7.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Impact Test | 36.0 J @Temperature 23.0 °C |
26.6 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 117 µm/m-°C @Temperature 0.000 - 100 °C |
65.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Hyflon® PFA P455 Perfluoroalkoxy (PFA)
- Solvay Specialty Polymers Ryton® QC160P Polyphenylene Sulfide (PPS)
- Silberline Silvet® 110-20-E
- Trelleborg Emerson & Cuming Stycast® 2057FR/11 Two-Component Epoxy Flame Retardant Encapsulant
- Crucible Steel 431 Chromium Steel
- DuPont Performance Polymers Kalrez® 8575 FFKM Perfluoroelastomer
- Arlon 30570R010 0.010" (0.254 mm) Uncured/Unsupported Silicone Rubber on a Release Carrier
- 3M Scotchcal™ 8000LF-37 Graphic Film
- 3M 4167 (Clear) Polyethylene Protective Tapes
- Huntsman PE2080 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved