SABIC Innovative Plastics Xenoy® 1102 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 1102 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| 6.40 J/cm @Temperature -30.0 °C |
12.0 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.94 J/cm @Temperature 0.000 °C |
13.0 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 78 FRT 5 PP, glass fibre, mod. of mech. properties
- Polykemi AB SCANMID 6 B11^ FX25 FR10 Nylon 6, Glass Fiber Reinforced, Flame Retardant
- DuPont Performance Polymers Delrin® 500CL BK601 Acetal Homopolymer (Unverified Data**)
- SABIC Innovative Plastics LNP THERMOCOMP RF007SXQ PA 66
- SABIC Innovative Plastics LNP THERMOCOMP TH0450C PUR (Asia Pacific)
- Borealis FT5232 Low Density Polyethylene
- A. Schulman CP80-01 Linear Low-Density Polyethylene
- ChevronTexaco ParaLux® 2401R Process Oil
- Amity Thermosets ATS 1613-R Phenolic Molding Nylon and glass Filler, Compression Molded
- Carpenter Hiperco® 50 Fe-Co-V Soft Magnetic Alloy, 0.15 mm Strip Heat Treated 843°C
Copyright © lookpolymers.com All Rights Reserved