Polymer Property : Flexural Yield Strength = 29000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	200 MPa	29000 psi	1.3 mm/min; ASTM D790
Ovation Polymers Opnyl OP66GF50 Nylon 66 Nylon 66-Glass reinforced(50%), high tensile strength, stiffness and HDT.Information provided by Ovation Polymers
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Owens Corning Glass Fiber Reinforced Nylon 6, 30 wt.% glass Nylons, as a group, are inert to most organic solvents. They resist alkalis and salt solutions and they are attacked by strong mineral acids and oxidizing agents. Data provided by the manufacturer,..
Flexural Yield Strength	200 MPa	29000 psi	ISO 178, ASTM D790
Nilit Nilamid A3 H G4 General Purpose 20% Glass Reinforced PA66 Description: Nilamid A3 H G4 is a general purpose, 20% glass fiber reinforced NYLON 66. This product combine good overall mechanical performance and impact strength with ease of processing.Key chara..
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM XH2315 TPI Resin Extem XH2315 Resin
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Asia Pacific) Extem XH2315 Resin
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Solvay Specialty Polymers Amodel® A-1230 L Polyphthalamide (PPA) (discontinued **) Amodel A-1230 L is a 30% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and ten..
Flexural Yield Strength	200 MPa	29000 psi	Conditioned; ASTM D790
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi..
Flexural Yield Strength	200 MPa	29000 psi	ISO 178
Solvay Specialty Polymers Ryton® R-7-120NA Polyphenylene Sulfide Compound (Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-7-120NA is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance moldi..
Flexural Yield Strength	200 MPa	29000 psi
Idemitsu Kosan XarecÂ® EA 543 SPS, 40% Glass Filled
Flexural Yield Strength	200 MPa	29000 psi
Idemitsu Kosan XarecÂ® WA 550 SPS, 30% Glass Filled Crystalline Polymer, Glass Filled. Used in Automotive and Industrial applications
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP IFL36R PA6.12 (Europe-Africa-Middle East) Internally lubricated PA6.12, containing Glass Fiber and PTFE
Flexural Yield Strength	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX152R PEI+PCE (Europe-Africa-Middle East) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Solvay Specialty Polymers AmodelÂ® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Conditioned) AmodelÂ® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s..
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET (Asia Pacific) PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon OX92182 PPS (Europe-Africa-Middle East) LNP* STAT-KON* OX92182 is a compound based on PPS-Branched resin containing Glass Fiber, Carbon Fiber, Mineral. Added features include : Electrically Conductive.This data was supplied by SABIC-IP fo..
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP PF1006HI005 PA 6 (Europe-Africa-Middle East) High Impact Nylon 6 compound containing Glass Fiber.
Flexural Yield Strength	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Flexural Yield Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Flexural Yield Strength	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific) Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Flexural Yield Strength	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Flexural Yield Strength	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX152R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Techmer ES HiFillÂ® TPX-HTN-03002 A 30% Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 30% Filler by WeightFeatures: Platable and High Temperature StrengthUL File Number: E157318Information provided by TP C..
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Clariant Renol PCSP0015 Polycarbonate, Carbon Fiber Filled Data provided by Clariant Masterbatches
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound (discontinued **) Black Polyphenylene Sulfide CompoundRyton® R-7 02 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compound wit..