SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.0 % | 4.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0026 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0026 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0072 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0072 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.6 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.6 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 140 MPa | 20300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 |
| 3.1 % | 3.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.00 GPa | 1020 ksi | 5 mm/min; ASTM D638 |
| 7.00 GPa | 1020 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 200 MPa | 29000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 200 MPa | 29000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 215 °C @Thickness 3.20 mm |
419 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 215 °C | 419 °F | Rate B/50; ASTM D1525 |
| 215 °C | 419 °F | Rate B/50; ISO 306 | |
| 225 °C | 437 °F | Rate B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3040-85A Thermoplastic Silicone Vulcanizate
- Polymer Resources PPX-G5 Modified-PPO, 5% Glass Reinforced
- Minelco Reclaimed Corderite
- Momentive Performance Materials Silplusâ„¢ 40 HS High Strength Heat Cured Rubber
- H.C. Starck Amperit® 782.054 Titanium Oxide (TiO2)
- SABIC Innovative Plastics LNP Thermocomp QF008R PA 6/10
- ChevronTexaco HDAX® SAE 30 Low Ash Gas Engine Oil
- Axiall EX 3114B Plenum Flexible PVC
Copyright © lookpolymers.com All Rights Reserved