Owens Corning Glass Fiber Reinforced Nylon 6, 30 wt.% glass

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	Owens Corning
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Owens Corning Glass Fiber Reinforced Nylon 6, 30 wt.% glass.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nylons, as a group, are inert to most organic solvents. They resist alkalis and salt solutions and they are attacked by strong mineral acids and oxidizing agents. Data provided by the manufacturer, Owens Corning.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ASTM D792
Water Absorption	1.3 %	1.3 %	24 hrs.; ASTM D570
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM D785
Tensile Strength, Ultimate	170 MPa	24700 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Modulus of Elasticity	7.24 GPa	1050 ksi	ASTM D638
Flexural Yield Strength	200 MPa	29000 psi	ASTM D790
Flexural Modulus	7.65 GPa	1110 ksi	ASTM D790
Compressive Strength	170 MPa	24700 psi	ASTM D695
Izod Impact, Notched	1.20 J/cm	2.25 ft-lb/in

Thermal Properties	Metric	English	Comments
CTE, linear	2.70 µm/m-°C @Temperature 20.0 °C	1.50 µin/in-°F @Temperature 68.0 °F	ASTM D696
Thermal Conductivity	0.836 - 1.64 W/m-K	5.80 - 11.4 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 1.8 MPa (264 psi)	211 °C	412 °F	ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	ASTM D257
Dielectric Constant	3.9 @Frequency 60 Hz	3.9 @Frequency 60 Hz	ASTM D150
Dielectric Strength	19.7 kV/mm	500 kV/in	ASTM D149
Arc Resistance	120 sec	120 sec	ASTM D495