SABIC Innovative Plastics EXTEM XH2315 TPI Resin
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Extem |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics EXTEM XH2315 TPI Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extem XH2315 Resin
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Water Absorption | 0.59 % @Time 173000 sec |
0.59 % @Time 48.0 hour |
ASTM D570 |
| Melt Flow | 4.0 g/10 min @Load 6.60 kg, Temperature 367 °C |
4.0 g/10 min @Load 14.6 lb, Temperature 693 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
| 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
| 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.23 GPa | 1484 ksi | 5 mm/min; ASTM D638 |
| 10.53 GPa | 1527 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 200 MPa | 29000 psi | 2 mm/min; ISO 178 |
| 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.00 GPa | 1310 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.860 J/cm | 1.61 ft-lb/in | ASTM D256 |
| 3.20 J/cm @Thickness 3.20 mm |
5.99 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature 23.0 - 150 °C |
8.89 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature 23.0 - 150 °C |
29.4 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 255 °C @Thickness 6.40 mm |
491 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 267 °C | 513 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Nilit Nilamid A3 H G4 General Purpose 20% Glass Reinforced PA66
- PSM Industries Pacific Sintered Metals Silicon Iron FS-1603 Powdered Metal
- Northstar Polymers GK-7 Low Viscosity Polyurethane Gel Cast
- Michelman® Michem® Emulsion 21930 Anionic Tung Oil emulsion
- SABIC Innovative Plastics LNP Thermocomp PK0049 PA 6 (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6
- UBE UBEPOL VCR617 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Braskem H 216 HOMO Polypropylene Homopolymer
- Techmer Lehvoss Compounds Luvotech™ J-4/30 BK PA6/12 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved