Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass-reinforced PPA. Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly. - Black: AT-1125 HS BK 324 - Natural: AT-1125 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.35 g/cc	0.0488 lb/in³	ISO 1183/A
Filler Content	25 %	25 %	Glass Fiber Reinforcement
Water Absorption	0.20 % @Time 86400 sec	0.20 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	174 MPa	25200 psi	ASTM D638
	190 MPa	27600 psi	ISO 527-2
Elongation at Break	2.5 %	2.5 %	ISO 527-2
	3.2 %	3.2 %	ASTM D638
Tensile Modulus	8.48 GPa	1230 ksi	ASTM D638
	8.89 GPa	1290 ksi	ISO 527-2
Flexural Strength	240 MPa	34800 psi	ISO 178
Flexural Yield Strength	200 MPa	29000 psi	Conditioned; ASTM D790
	255 MPa	37000 psi	ASTM D790
Flexural Modulus	7.58 GPa	1100 ksi	ASTM D790
	7.58 GPa	1100 ksi	Conditioned; ASTM D790
	7.79 GPa	1130 ksi	ISO 178
Izod Impact, Notched	0.850 J/cm	1.59 ft-lb/in	Conditioned; ASTM D256
	1.20 J/cm	2.25 ft-lb/in	ASTM D256
	8.00 J/cm	15.0 ft-lb/in	Conditioned; ASTM D256
	11.0 J/cm	20.6 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	8.80 kJ/m²	4.19 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.880 J/cm²	4.19 ft-lb/in²	ISO 179/1eA
Dart Drop, Total Energy	9.36 J	6.90 ft-lb	Conditioned; ASTM D3763
	13.8 J	10.2 ft-lb	ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	311 °C	592 °F	Peak; ASTM D3418
	311 °C	592 °F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	279 °C	534 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	235 °C	455 °F	Unannealed; ASTM D648
	280 °C	536 °F	Unannealed; ISO 75-2/A

Processing Properties	Metric	English	Comments
Feed Temperature	79.4 °C	175 °F	Hopper Temperature
Rear Barrel Temperature	304 - 318 °C	579 - 604 °F
Front Barrel Temperature	316 - 329 °C	601 - 624 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	135 °C	275 °F
Drying Temperature	121 °C	250 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.10 %	0.10 %

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
	Impact Modifier
Appearance	Black
	Natural Color
Automotive Specifications	ASTM D4000 PA123 G25
	ASTM D4000 PPA0111 G25 KD160 KN075 LD002 PN080 YI250
	ASTM D6779 PA123G25
	ISO 1874 PA6T/6I/66-HI, MH, 12-080, GF25
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Dimensional Stability
	Heat Stabilized
	High Heat Resistance
	Impact Modified
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Appliances
	Automotive Applications
	Automotive Electronics
	Automotive Under the Hood
	Bearings
	Connectors
	Fuel Lines
	General Purpose
	Housings
	Industrial Applications
	Industrial Parts
	Lawn and Garden Equipment
	Machine/Mechanical Parts
	Metal Replacement