SABIC Innovative Plastics LNP LUBRICOMP IFL36R PA6.12 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP IFL36R PA6.12 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Internally lubricated PA6.12, containing Glass Fiber and PTFE
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 148 MPa | 21500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 198 MPa | 28700 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 200 MPa | 29000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
15.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 101 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Heatbath/Park Wire Annealing Salt Neutral Salt
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.003" thick)
- Techmer ES Luriblend® TPU T/AL27 Aramid Fiber Filled
- Elektro-Isola G-Etronax EP 22 Epoxy, Glass Fabric Reinforcement, Light Yellow, Tubes
- ExxonMobil 220 Mobil DTE PM Series
- Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.65 g/cc Green Density
- Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, 50% RH
- Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed
- Spartech Solarex® K High Heat Weatherable Copolyester Sign Grade Sheet
- PolyOne LubriOne™ ATH-05KV/000 Acetal (POM) Homopolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved