Polymer Property : Tensile Strength, Yield = 60.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Compression; ISO 527
Raschig Group 2567 AMC
Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Compression; ISO 527
Raschig Group 2568 AMC
Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Compression; ISO 527
Raschig Group 5553 DAP
Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Tensile Strength, Yield 50.0 - 60.0 MPa
7250 - 8700 psi
Injection; ISO 527
Raschig Group AMPLA® 7500 melamine-modified polyester
Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Tensile Strength, Yield 40.0 - 60.0 MPa
5800 - 8700 psi
Compression; ISO 527
Raschig Group MELOPLAS® 182 MF
Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf..
Tensile Strength, Yield 45.0 - 60.0 MPa
6530 - 8700 psi
Compression; ISO 527
Raschig Group MELOPLAS® 2500 MF
Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Compression; ISO 527
Raschig Group RALUPOL® 4385 UP
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Compression; ISO 527
Raschig Group SURAPLAST 54 UPA
Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
7250 - 8700 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6008 Polyvinylidene Fluoride (PVDF)  (Unverified Data**)
Solef® 6008 PVDF homopolymer is a low-viscosity PVDF resin and is typically processed by injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
7250 - 8700 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF)  (Unverified Data**)
Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
7250 - 8700 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)  (Unverified Data**)
Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield 56.0 - 60.0 MPa
8120 - 8700 psi
50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound  (discontinued **)
Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall..
Tensile Strength, Yield 45.0 - 60.0 MPa
6530 - 8700 psi
ISO-DIS 527
Schwartz Technical Plastics LAMIGAMID® 400 Cast Polyamide 6, Elastomer Modified, Dry
Application: gear-wheels, chain-wheels, hydrocyclones, housings, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield 40.0 - 60.0 MPa
5800 - 8700 psi
ISO-DIS 527
Schwartz Technical Plastics LAMINEX® 2101 Cotton Fabric, Phenolic Resin Impregnated
Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield 40.0 - 60.0 MPa
5800 - 8700 psi
ISO-DIS 527
Schwartz Technical Plastics LAMINEX® 2141 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled
Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm
7250 - 8700 psi

@Thickness 0.0787 in
50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF)
Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Prope..
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm
7250 - 8700 psi

@Thickness 0.0787 in
50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6008 Polyvinylidene Fluoride (PVDF)
Solef® 6008 PVDF homopolymer is a low-viscosity PVDF resin and is typically processed by injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D..
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm
7250 - 8700 psi

@Thickness 0.0787 in
50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF)
Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Features: Homopolymer; Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3417 54.0 to 6..
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm
7250 - 8700 psi

@Thickness 0.0787 in
50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Features: High Viscosity; HomopolymerAdditional Properties: Crystallizat..
Tensile Strength, Yield 45.0 - 60.0 MPa

@Thickness 2.00 mm
6530 - 8700 psi

@Thickness 0.0787 in
50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF)
Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 53...
Tensile Strength, Yield 50.0 - 60.0 MPa
7250 - 8700 psi
ISO 527
Beijing Ranger Chem BLUESTAR® 1084 PBT
Can be used directly for spinning, and producing color concentrates. It can also be used for production after reinforcement & compounding.Information provided by Beijing Ranger Chemical Co.
Tensile Strength, Yield 50.0 - 60.0 MPa
7250 - 8700 psi
ISO 527
Beijing Ranger Chem BLUESTAR® 1110 PBT
Can be used directly for spinning, or it can be used after reinforcement & compounding. It can also be used to produce cable sheath through tackificationInformation provided by Beijing Ranger Chemic..
Tensile Strength, Yield 50.0 - 60.0 MPa
7250 - 8700 psi
ISO 527
Beijing Ranger Chem BLUESTAR® 1135 PBT
Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co.
Tensile Strength, Yield 45.0 - 60.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
6530 - 8700 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF)  (Unverified Data**)
Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield 45.0 - 60.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
6530 - 8700 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF)  (discontinued **)
Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield 45.0 - 60.0 MPa
6530 - 8700 psi
Compression; ISO 527
Raschig Group MELOPLAS® 180 MF
Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing ..
Tensile Strength, Yield 50.0 - 60.0 MPa
7250 - 8700 psi
ISO 527
Beijing Ranger Chem BLUESTAR® 1120 PBT
Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co.
Tensile Strength, Yield 28.0 - 60.0 MPa
4060 - 8700 psi
Average value: 42.2 MPa Grade Count:17
Overview of materials for Acrylic, Impact Modified, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified, Molded". Each property range of values reported is minimum and maximum values ..
Tensile Strength, Yield 13.8 - 60.0 MPa
2000 - 8700 psi
Average value: 29.2 MPa Grade Count:76
Overview of materials for Polypropylene with 40% Talc Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are..
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Average value: 55.8 MPa Grade Count:6
Overview of materials for Polytrimethylene Terephthalate (PTT)
This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val..