Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF)  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.75 - 1.80 g/cc
1.75 - 1.80 g/cc
ASTM D792
Water Absorption <= 0.040 %

@Temperature 23.0 °C,
Time 86400 sec
 <= 0.040 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.020 - 0.030 cm/cm
0.020 - 0.030 in/in
Melt Flow 7.0 - 13 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 7.0 - 13 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
10 - 20 g/10 min

@Load 5.00 kg,
Temperature 230 °C
 10 - 20 g/10 min

@Load 11.0 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 73 - 80

@Thickness 2.00 mm,
Time 1.00 sec
 73 - 80

@Thickness 0.0787 in,
Time 0.000278 hour
 ASTM D2240
Tensile Strength at Break 30.0 - 50.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
 4350 - 7250 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
 Type IV, 50 mm/min; ASTM D638
Tensile Strength, Yield 45.0 - 60.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
 6530 - 8700 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
 Type IV, 50 mm/min; ASTM D638
Elongation at Break 20 - 300 %

@Thickness 2.00 mm,
Temperature 23.0 °C
 20 - 300 %

@Thickness 0.0787 in,
Temperature 73.4 °F
 Type IV, 50 mm/min; ASTM D638
Elongation at Yield 5.0 - 10 %

@Thickness 2.00 mm,
Temperature 23.0 °C
 5.0 - 10 %

@Thickness 0.0787 in,
Temperature 73.4 °F
 Type IV, 50 mm/min; ASTM D638
Tensile Modulus 1.40 - 2.20 GPa

@Thickness 2.00 mm,
Temperature 23.0 °C
 203 - 319 ksi

@Thickness 0.0787 in,
Temperature 73.4 °F
 Type IV, 1.0 mm/min; ASTM D638
Impact 37.4 - 107

@Thickness 4.00 mm
 37.4 - 107

@Thickness 0.157 in
 J/m Charpy Notched Impact Strength; 2 m/s; ASTM D6110
Coefficient of Friction, Dynamic 0.15 - 0.35
0.15 - 0.35
vs. Itself; ASTM D1894
Coefficient of Friction, Static 0.20 - 0.40
0.20 - 0.40
vs. Itself; ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0 - 10

@Load 1.00 kg
 5.0 - 10

@Load 2.20 lb
 CS-10 Wheel; ASTM D4060
Thermal Properties Metric English Comments
Heat of Fusion 53.0 - 60.0 J/g
22.8 - 25.8 BTU/lb
Crystallization Heat; ASTM D3418
53.0 - 60.0 J/g
22.8 - 25.8 BTU/lb
ASTM D3418
CTE, linear, Parallel to Flow 140 µm/m-°C
77.8 µin/in-°F
ASTM D696
Specific Heat Capacity 1.20 J/g-°C

@Temperature 23.0 °C
 0.287 BTU/lb-°F

@Temperature 73.4 °F
 ASTM C351
1.60 J/g-°C

@Temperature 100 °C
 0.382 BTU/lb-°F

@Temperature 212 °F
 ASTM C351
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 162 - 168 °C
324 - 334 °F
ASTM D3418
Crystallization Temperature 133 - 140 °C
271 - 284 °F
Peak, DSC; ASTM D3418
Glass Transition Temp, Tg -40.0 °C
-40.0 °F
ASTM D4065
Flammability, UL94 V-0

@Thickness 0.100 mm
 V-0

@Thickness 0.00394 in
 UL 94
Oxygen Index 44 %

@Thickness 3.00 mm
 44 %

@Thickness 0.118 in
 ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D257
Dielectric Strength 20.0 - 25.0 kV/mm

@Thickness 1.00 mm,
Temperature 23.0 °C
 508 - 635 kV/in

@Thickness 0.0394 in,
Temperature 73.4 °F
 ASTM D149
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Homopolymer
Medium Viscosity
Generic PVDF
Processing Method Film Extrusion
Injection Molding