Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer Solvay Specialty Polymers
Trade Name Solef®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Properties: Charpy Notched Impact Strength - ASTM D6110 (23°C, 4.00 mm): 25.0 to 75.0 J/m; Coefficient of Friction - ASTM D1894 0.150 to 0.350; Coefficient of Friction - ASTM D1894 0.200 to 0.400; Crystallization Heat - ASTM D3417 54.0 to 60.0 J/g; Crystallization Point - ASTM D3418 137 to 144 °C; Heat of Fusion - ASTM D3417 58.0 to 67.0 J/g; Mold Shrinkage - 2.0 to 3.0 %Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.75 - 1.80 g/cc
0.0632 - 0.0650 lb/in³
ASTM D792
Water Absorption <= 0.040 %

@Time 86400 sec
 <= 0.040 %

@Time 24.0 hour
 ISO 62
Melt Flow 30 - 40 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 30 - 40 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 73 - 80
73 - 80
1 sec, 2.00 mm; ISO 868
Tensile Strength at Break 30.0 - 50.0 MPa

@Thickness 2.00 mm
 4350 - 7250 psi

@Thickness 0.0787 in
 50 mm/min; ASTM D638
Tensile Strength, Yield 50.0 - 60.0 MPa

@Thickness 2.00 mm
 7250 - 8700 psi

@Thickness 0.0787 in
 50 mm/min; ASTM D638
Elongation at Break 20 - 300 %
20 - 300 %
50 mm/min; ASTM D638
Elongation at Yield 5.0 - 10 %
5.0 - 10 %
50 mm/min; ASTM D638
Tensile Modulus 1.80 - 2.60 GPa

@Thickness 2.00 mm
 261 - 377 ksi

@Thickness 0.0787 in
 1.0 mm/min; ASTM D638
Taber Abrasion, mg/1000 Cycles 5.0 - 10
5.0 - 10
CS-10 Wheel, 1000 g; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 140 µm/m-°C

@Temperature 0.000 - 40.0 °C
 77.8 µin/in-°F

@Temperature 32.0 - 104 °F
 1
Specific Heat Capacity 1.20 J/g-°C

@Temperature 23.0 °C
 0.287 BTU/lb-°F

@Temperature 73.4 °F
 ASTM C351
1.60 J/g-°C

@Temperature 100 °C
 0.382 BTU/lb-°F

@Temperature 212 °F
 ASTM C351
Thermal Conductivity 0.200 W/m-K

@Temperature 23.0 °C
 1.39 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
 ASTM C177
Melting Point 170 - 175 °C
338 - 347 °F
DSC
Crystallization Temperature 134 - 144 °C
273 - 291 °F
Peak; ASTM D3418
Vicat Softening Point 135 - 145 °C
275 - 293 °F
Rate A (50°C/h), Loading 2 (50 N)
Glass Transition Temp, Tg -40.0 °C
-40.0 °F
ASTM E1356
Flammability, UL94 V-0

@Thickness 0.100 mm
 V-0

@Thickness 0.00394 in
Oxygen Index 44 %

@Thickness 3.00 mm
 44 %

@Thickness 0.118 in
 ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D257
Dielectric Constant 7.0 - 10

@Frequency 1000 Hz
 7.0 - 10

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 20.0 - 25.0 kV/mm

@Thickness 1.00 mm
 508 - 635 kV/in

@Thickness 0.0394 in
 ASTM D149
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color White
Form Pellets
Processing Technique Extrusion; Injection Molding