Raschig Group RALUPOL® 4806 UP

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS
Manufacturer	Raschig Group
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Raschig Group RALUPOL® 4806 UP.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 804. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression molding Primary application: Contact bridges, Relays, Circuit breakers (RCD/MCB)Information provided by the Raschig Group

Physical Properties	Metric	English	Comments
Specific Gravity	1.90 - 2.10 g/cc	1.90 - 2.10 g/cc	ISO 1183
Apparent Bulk Density	0.750 - 0.950 g/cc	0.0271 - 0.0343 lb/in³	ISO 60
Water Absorption	<= 0.50 % @Temperature 23.0 °C, Time 86400 sec	<= 0.50 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
Linear Mold Shrinkage	0.0020 - 0.0050 cm/cm	0.0020 - 0.0050 in/in	Compression; ISO 2577
	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	Injection; ISO 2257

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
	40.0 - 70.0 MPa	5800 - 10200 psi	Injection; ISO 527
Modulus of Elasticity	9.00 - 11.0 GPa	1310 - 1600 ksi	Injection and Compression; ISO 527
Flexural Strength	70.0 - 100 MPa	10200 - 14500 psi	Compression; ISO 178
	110 - 130 MPa	16000 - 18900 psi	Injection; ISO 178
Flexural Modulus	10.0 - 13.0 GPa	1450 - 1890 ksi	Compression; ISO 178
	13.0 - 16.0 GPa	1890 - 2320 ksi	Injection; ISO 178
Compressive Strength	150 - 200 MPa	21800 - 29000 psi	ISO 604
Charpy Impact Unnotched	0.500 - 1.00 J/cm² @Temperature 23.0 °C	2.38 - 4.76 ft-lb/in² @Temperature 73.4 °F	Compression; ISO 179/ 1eU
	0.700 - 1.00 J/cm² @Temperature 23.0 °C	3.33 - 4.76 ft-lb/in² @Temperature 73.4 °F	Injection; ISO 179/ 1eU
Charpy Impact, Notched	0.250 - 0.350 J/cm² @Temperature 23.0 °C	1.19 - 1.67 ft-lb/in² @Temperature 73.4 °F	Compression; ISO 179/ 1eA
	0.350 - 0.500 J/cm² @Temperature 23.0 °C	1.67 - 2.38 ft-lb/in² @Temperature 73.4 °F	Injection; ISO 179/ 1eA

Thermal Properties	Metric	English	Comments
CTE, linear	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Thermal Conductivity	0.900 - 1.10 W/m-K	6.25 - 7.63 BTU-in/hr-ft²-°F	DIN 52 612
Maximum Service Temperature, Air	170 °C	338 °F	20,000 h; IEC 216/T1
	220 °C	428 °F	< 50 h; IEC 216/T1
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	Compression and Injection; ISO 75-C
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in
Shrinkage	<= 0.10 % @Temperature 110 °C, Time 605000 sec	<= 0.10 % @Temperature 230 °F, Time 168 hour	Post Shrinkage; ISO 2577

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 - 1.00e+15 ohm-cm	1.00e+14 - 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 - 1.00e+14 ohm	1.00e+13 - 1.00e+14 ohm	IEC 60093
Dielectric Constant	4.0 - 5.0 @Frequency 1.00e+6 Hz	4.0 - 5.0 @Frequency 1.00e+6 Hz	IEC 60250
	5.0 - 6.0 @Frequency 100 Hz	5.0 - 6.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	25.0 - 35.0 kV/mm	635 - 889 kV/in	IEC 60243-1
Dissipation Factor	0.010 - 0.030 @Frequency 100 Hz	0.010 - 0.030 @Frequency 100 Hz	IEC 60250
	0.010 - 0.030 @Frequency 1.00e+6 Hz	0.010 - 0.030 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	PTI; IEC 60112

Processing Properties	Metric	English	Comments
Shelf Life	6.00 Month @Temperature 15.0 - 25.0 °C	6.00 Month @Temperature 59.0 - 77.0 °F

Descriptive Properties	Value	Comments
Arc Resistance	4 Stufe	ASTM D495
Glow wire ignitability test	930/1	IEC 60695 2-13
Glow-wire flammability test	960/1	IEC 60695 2-12
Water Absorption	<35 mg	ISO 62; 24h / 23°C