Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | Injection; ISO 527 |
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | Injection; ISO 527 |
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
Tensile Strength, Yield | 40.0 - 60.0 MPa | 5800 - 8700 psi | Compression; ISO 527 |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Tensile Strength, Yield | 45.0 - 60.0 MPa | 6530 - 8700 psi | Compression; ISO 527 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
7250 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
7250 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength, Yield | 45.0 - 60.0 MPa | 6530 - 8700 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 400 Cast Polyamide 6, Elastomer Modified, Dry Application: gear-wheels, chain-wheels, hydrocyclones, housings, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMINEX® 2101 Cotton Fabric, Phenolic Resin Impregnated Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMINEX® 2141 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm |
7250 - 8700 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF) Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Prope.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm |
7250 - 8700 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6008 Polyvinylidene Fluoride (PVDF) Solef® 6008 PVDF homopolymer is a low-viscosity PVDF resin and is typically processed by injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm |
7250 - 8700 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF) Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Features: Homopolymer; Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3417 54.0 to 6.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm |
7250 - 8700 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Features: High Viscosity; HomopolymerAdditional Properties: Crystallizat.. |
|||
Tensile Strength, Yield | 45.0 - 60.0 MPa @Thickness 2.00 mm |
6530 - 8700 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF) Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 53... |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 527 |
Beijing Ranger Chem BLUESTAR® 1084 PBT Can be used directly for spinning, and producing color concentrates. It can also be used for production after reinforcement & compounding.Information provided by Beijing Ranger Chemical Co. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 527 |
Beijing Ranger Chem BLUESTAR® 1110 PBT Can be used directly for spinning, or it can be used after reinforcement & compounding. It can also be used to produce cable sheath through tackificationInformation provided by Beijing Ranger Chemic.. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 527 |
Beijing Ranger Chem BLUESTAR® 1135 PBT Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co. |
|||
Tensile Strength, Yield | 45.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
6530 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength, Yield | 45.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
6530 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF)
(discontinued **) Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength, Yield | 45.0 - 60.0 MPa | 6530 - 8700 psi | Compression; ISO 527 |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 527 |
Beijing Ranger Chem BLUESTAR® 1120 PBT Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co. |
|||
Tensile Strength, Yield | 28.0 - 60.0 MPa | 4060 - 8700 psi | Average value: 42.2 MPa Grade Count:17 |
Overview of materials for Acrylic, Impact Modified, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified, Molded". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Yield | 13.8 - 60.0 MPa | 2000 - 8700 psi | Average value: 29.2 MPa Grade Count:76 |
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Average value: 55.8 MPa Grade Count:6 |
Overview of materials for Polytrimethylene Terephthalate (PTT) This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val.. |