Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006 TPI Blend High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also ha.. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend High heat amorphous TPI Blend, Chemical Resistant |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1016 TPI Blend High heat amorphous TPI Blend, Chemical Resistant, High Flow |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant, High Flow |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant, High Flow |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Extem UH1016M TPI Blend High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Extem UH1016M TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | SABIC - Japan Method |
SABIC Innovative Plastics Lexan® LF1520 PC (Asia Pacific) |
|||
Tensile Strength, Yield | 112 - 200 MPa | 16200 - 29000 psi | Average value: 171 MPa Grade Count:12 |
Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl PX7446 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KFI15 ACETAL LNP* LUBRICOMP* KFI15 is a compound based on Acetal containing 25% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® ENH4550 PBT 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON ZE0039 MODIFIED POLYPHENYLENE (Asia Pacific) LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE (Asia Pacific) LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON ZE0039 PPO LNP* STAT-KON* ZE0039 is a compound based on PPO resin containing 15% Carbon Fiber. Added features of this grade includes: Flame Retardant, Electrically Conductive. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D638 |
Techmer ES Luriblend® PC CF15 TL6 BK 15% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Composites, I.. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D638 |
SABIC Innovative Plastics NORYL PX4605 PPE+PS PPE+PS blend. 20% Glass reinforced. High heat. Dimensional stability. Suitable for automotive and E/E applications. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific) LNP* Stat-kon* DEL339XF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant,.. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK LNP THERMOCOMP* LFZ42XXC is a compound based on Polyetheretherketone resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage.This data was supplied by SABIC.. |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL GTX APS130 PPE+PPS (Asia Pacific) PPE+PPS GF30% |
|||
Tensile Strength, Yield | 112 MPa | 16200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL APS130 PPE+PPS (Asia Pacific) |