SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DEL339XF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0031 cm/cm @Time 86400 sec |
0.0031 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| 114 MPa | 16500 psi | ASTM D638 | |
| Tensile Strength, Yield | 112 MPa | 16200 psi | ISO 527 |
| 114 MPa | 16500 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Elongation at Yield | 1.6 % | 1.6 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 10.34 GPa | 1500 ksi | 50 mm/min; ASTM D638 |
| 10.95 GPa | 1588 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 164 MPa | 23800 psi | ISO 178 |
| 179 MPa | 26000 psi | ASTM D790 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| 9.50 GPa | 1380 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.57 J/cm | 6.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 14.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.78 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 14.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+7 - 1.00e+9 ohm | 1.00e+7 - 1.00e+9 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® FR23 ABS
- Polykemi AB SCANMID 6 B22^ E F15 Nylon 6, Glass Fiber Reinforced, Modified
- Eastman Tenite Butyrate 465E2R30012 Natural, Trsp Cellulose Acetate Butyrate (discontinued **)
- Kazanorgsintez 153-15 Composition of Low Density Polyethylene, Crack-Proof
- Ineos Nova 1510 High Heat Crystal Polystyrene
- Lubriplate CLEARPLEX 2 Aluminum Complex USP Mineral Oil-Based Food Machinery Grade Grease
- SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Europe-Africa-Middle East)
- Diamond Polymers ABS 2510
- Barlog Plastics KEBAFORM C 8027 POM Copolymer, 30% mineral reinforced
Copyright © lookpolymers.com All Rights Reserved