 POLYMER SEARCH

SABIC Innovative Plastics Noryl PX7446 PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl PX7446 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %

@Temperature 23.0 °C
 0.25 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0030 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 10 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
11.7 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 11.7 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 112 MPa
16200 psi
Type I, 5 mm/min; ASTM D 638
114 MPa
16500 psi
5 mm/min; ISO 527
Tensile Strength, Yield 112 MPa
16200 psi
Type I, 5 mm/min; ASTM D 638
114 MPa
16500 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
2.9 %
2.9 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
2.9 %
2.9 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 6.15 GPa
892 ksi
5 mm/min; ASTM D 638
6.57 GPa
953 ksi
1 mm/min; ISO 527
Flexural Strength 174 MPa
25200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 181 MPa
26300 psi
2 mm/min; ISO 178
Flexural Modulus 5.70 GPa
827 ksi
1.3 mm/min, 50 mm span; ASTM D 790
6.22 GPa
902 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.960 J/cm

@Temperature 23.0 °C
 1.80 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
1.09 J/cm

@Temperature -30.0 °C
 2.04 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
Izod Impact, Unnotched 5.12 J/cm

@Temperature 23.0 °C
 9.59 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 19.0 J

@Temperature 23.0 °C
 14.0 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 31.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
55.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 31.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 63.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
63.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
156 °C

@Thickness 3.20 mm
 313 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 164 °C
327 °F
Rate B/50; ASTM D 1525
164 °C
327 °F
Rate B/50; ISO 306
165 °C
329 °F
Rate B/120; ISO 306