SABIC Innovative Plastics LNP LUBRICOMP KFI15 ACETAL
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFI15 ACETAL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KFI15 is a compound based on Acetal containing 25% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 102 MPa | 14800 psi | Type I, 5 mm/min; ASTM D638 |
| 118 MPa | 17100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.71 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| 9.26 GPa | 1340 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 172 MPa | 24900 psi | ISO 178 |
| 176 MPa | 25500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.85 GPa | 1140 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.01 GPa | 1160 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.760 J/cm | 1.42 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.37 J/cm | 10.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 713 (NG) Synthetic Oil
- Mitsui Fybrel® E 795 Polyolefin Synthetic Pulp, Dry Processes (discontinued **)
- Huntsman AVALON® 90 AKU Thermoplastic Polyurethane
- Struktol V-MAT G Processing Additive, Matting Agent
- SABIC Innovative Plastics NORYL GTX RNX130 PPE+PS+PA
- Teknor Apex Telcar® TL-1654A Thermoplastic Elastomer
- Diamond Polymers NPP30-0500 GF30 BLACK HOMOPOLYMER 30% Glass Filled Black Homopolymer Polypropylene
- Abatron AboCast 8103-28 High-Performance Dielectric Epoxy
- Arlon R31961R019 0.019" (0.483 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved