SABIC Innovative Plastics NORYL PX4605 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX4605 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. 20% Glass reinforced. High heat. Dimensional stability. Suitable for automotive and E/E applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 112 MPa | 16200 psi | ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.4 % | 2.4 % | ASTM D638 |
| Tensile Modulus | 7.56 GPa | 1100 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 148 MPa | 21500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 5.24 GPa | 760 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 5.52 GPa | 801 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| 1.00 J/cm @Temperature -40.0 °C |
1.87 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 20.0 J @Temperature 23.0 °C |
14.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C @Thickness 3.20 mm |
309 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Shakespeare WP-120 diameter 0.5 mm Weft Polyester Monofilament
- SK Chemicals SKYPEL M555DH General Grade
- Goodfellow Carbon-Carbon Composite
- CP-Polymer-Technik Wellamid® 6600 CF10 HWCP 10% Carbon Fiber Nylon 66, Heat Stabilized, Conditioned
- Chosun Refractories BLC Lance Castable
- Eurostar Star L PA66 D51 PA66, Injection Molded
- Colorite Polymers 9002 General Purpose Vinyl Compound
- Asahi Kasei Thermylene® P-10FG-2100 10% Glass Fiber Reinforced
- LATI Laticonther 80 GR/50 PPS, 50% Graphite Reinforced
- Henkel Hysol EA 9820 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved