- SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE
SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE
| Category | Polymer , Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 1.21 g/cc | 0.0437 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.00080 cm/cm @Time 86400 sec |
0.00080 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527 |
| 112 MPa | 16200 psi | ASTM D 638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | ISO 527 |
| 112 MPa | 16200 psi | ASTM D 638 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.2 % | 1.2 % | ASTM D 638 | |
| Elongation at Yield | 1.0 % | 1.0 % | ISO 527 |
| 1.2 % | 1.2 % | ASTM D 638 | |
| Tensile Modulus | 10.97 GPa | 1591 ksi | 1 mm/min; ISO 527 |
| 11.72 GPa | 1700 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D 790 |
| 150 MPa | 21800 psi | ISO 178 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D 790 |
| 10.6 GPa | 1540 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.67 J/cm @Temperature 23.0 °C |
5.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 29.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Old Hickory Thomas Tennessee Ball Clay
- Raschig Group 2557 AMC Polyester
- PolyOne Geon™ Vinyl Flexible 90043 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Pyrotek A-1 Glass Fiber Core Rope
- SABIC Innovative Plastics Lexan® 144H PC (Europe-Africa-Middle East)
- LyondellBasell Alathon® L5008HP High Density Polyethylene, Pressure Pipe Extrusion Grade
- A. Schulman POLYBATCH™ Blue LL40445/2 Concentrate Based In LLDPE
- Chevron Phillips MarFlex® 7105D Polyethylene; LLDPE
- 3M Scotchcal™ IJ5000 Reflective Graphic Film'
- Overview of materials for Acrylic, Gamma Radiation Resistant, Molded
Copyright © lookpolymers.com All Rights Reserved