SABIC Innovative Plastics EXTEM UH1006M TPI Blend
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Extem |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics EXTEM UH1006M TPI Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat amorphous TPI Blend, Chemical Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % @Time 173000 sec |
0.60 % @Time 48.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 6.60 kg, Temperature 400 °C |
6.0 g/10 min @Load 14.6 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
| 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 19 % | 19 % | 5 mm/min; ISO 527 |
| 20 % | 20 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D638 |
| 9.0 % | 9.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| 3.80 GPa | 551 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 154 MPa | 22300 psi | 2 mm/min; ISO 178 |
| 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.6 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 47.0 µm/m-°C @Temperature 23.0 - 150 °C |
26.1 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 257 °C | 495 °F | Rate B/50; ASTM D1525 |
| 262 °C | 504 °F | Rate B/50; ISO 306 | |
| 263 °C | 505 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Nye Lubricants 748C (RL) Synthetic Oil
- SABIC Innovative Plastics Lexan® HF1130R PC
- PolyOne Edgetek® QT-20MN/000 natural HI Syndiotactic Polystyrene (SPS)
- Lehmann & Voss LUVOCOM® 50-1396 Polycarbonate, with carbon fiber, glass fiber and PTFE, electrically conducting
- Teknor Apex APEX® 130-Y Polyvinyl Chloride, Flexible
- PlastxWorld Veroplas PB2000 Nylon 66
- Lubrizol Estane® 2103-80PF Thermoplastic Polyurethane Elastomer
- Asahi Glass Fluon® PB3360T 60% Bronze, PTFE Filled Compound
- ACC QSil 58 QSI Quantum Silicones 50 Durometer Condensation Cure for Potting
Copyright © lookpolymers.com All Rights Reserved