Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 80.0 - 90.0 MPa | 11600 - 13100 psi | Injection; ISO 527 |
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Tensile Strength, Yield | 80.0 - 90.0 MPa | 11600 - 13100 psi | Injection; ISO 527 |
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Tensile Strength, Yield | 50.0 - 90.0 MPa | 7250 - 13100 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Tensile Strength, Yield | 50.0 - 90.0 MPa | 7250 - 13100 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
Tensile Strength, Yield | 60.0 - 90.0 MPa | 8700 - 13100 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Tensile Strength, Yield | 70.0 - 90.0 MPa | 10200 - 13100 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Tensile Strength, Yield | 50.0 - 90.0 MPa | 7250 - 13100 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Tensile Strength, Yield | 60.0 - 90.0 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
8700 - 13100 psi @Thickness 0.157 in, Temperature 73.4 °F |
depending on color; ISO 527-2/5 |
PolyOne Bergamid™ A70 GK30 H Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
Tensile Strength, Yield | 13.0 - 90.0 MPa | 1890 - 13100 psi | Average value: 66.5 MPa Grade Count:109 |
Overview of materials for Acetal Homopolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Yield | 20.0 - 90.0 MPa @Temperature -40.0 - 120 °C |
2900 - 13100 psi @Temperature -40.0 - 248 °F |
Average value: 45.0 MPa Grade Count:1 |
Overview of materials for Nylon 6, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Mineral Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Yield | 25.0 - 90.0 MPa | 3630 - 13100 psi | Average value: 63.5 MPa Grade Count:41 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Tensile Strength, Yield | 82.0 - 90.0 MPa | 11900 - 13100 psi | Average value: 88.0 MPa Grade Count:5 |
Overview of materials for Nylon 6-3 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6-3". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Tensile Strength, Yield | 35.0 - 90.0 MPa | 5080 - 13100 psi | Average value: 65.7 MPa Grade Count:54 |
Overview of materials for Nylon 6, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum v.. |
|||
Tensile Strength, Yield | 40.0 - 90.0 MPa | 5800 - 13100 psi | Average value: 61.0 MPa Grade Count:10 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Yield | 47.0 - 90.0 MPa | 6820 - 13100 psi | Average value: 62.4 MPa Grade Count:26 |
Overview of materials for Polyethylene Terephthalate (PET), Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Unreinforced". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Yield | 25.0 - 90.0 MPa | 3630 - 13100 psi | Average value: 59.6 MPa Grade Count:99 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |