PolyOne Bergamid™ A70 GK30 H Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ A70 GK30 H Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ±0.03 g/cm³; DIN 53479 |
| Ash | 30 % | 30 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 - 90.0 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
8700 - 13100 psi @Thickness 0.157 in, Temperature 73.4 °F |
depending on color; ISO 527-2/5 |
| Elongation at Yield | 2.5 - 4.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
2.5 - 4.0 % @Thickness 0.157 in, Temperature 73.4 °F |
depending on color; ISO 527-2/5 |
| Tensile Modulus | 4.00 - 4.80 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
580 - 696 ksi @Thickness 0.157 in, Temperature 73.4 °F |
depending on color; ISO 527-2/1 |
| Charpy Impact Unnotched | 0.250 - 0.420 J/cm² @Temperature 23.0 °C |
1.19 - 2.00 ft-lb/in² @Temperature 73.4 °F |
depending on color; ISO 179/1eU |
| Charpy Impact, Notched | 2.50 - 4.00 J/cm² @Temperature 23.0 °C |
11.9 - 19.0 ft-lb/in² @Temperature 73.4 °F |
depending on color; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ISO 3146 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| 220 °C | 428 °F | Short Time; IEC 60216 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL 94 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 60.0 kV/mm | 1520 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 500 V | 500 V | Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Heat Stabilized | |
| Filler / Reinforcement | Glass Bead, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| K-Value | 74.0 to 78.0 | No Standard; 96% H2SO4 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® A 3000 AE Expandable Polystyrene, Standard Flame Retardant
- Network Polymers Softflex® 8103
- Pacific Sintered Materials FCC-214-S(HT) High Carbon Copper Steel Powdered Metal
- Polykemi AB POLYfill PPH GF5040 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- LG Chemical XR440 ABS, Low Emission High Heat ABS
- Teknor Apex APEX® 90-A471R-85-NT Polyvinyl Chloride, Flexible
- Chosun Refractories LPCT-18PI Lance Castable
- BASF Ultramid® A3HG7 BK 00564 35% Glass Filled PA66 (Conditioned)
- GEHR Plastics PVC-U Polyvinylchloride
Copyright © lookpolymers.com All Rights Reserved