Polymer Property : Tensile Strength, Yield = 108 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 108 - 200 MPa | 15700 - 29000 psi | Average value: 133 MPa Grade Count:4 |
| Overview of materials for Nylon 612, Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of.. |
|||
| Tensile Strength, Yield | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUCON CP2100-KA02 PC+CF Description Injection Molding Grade, PC+CF, Electrostatic Dissipation, Low Surface ResistanceApplication: LCD Tray, HDD BracketCAS No. 103598-77-2 and 7440-44-0Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUPOS GP2305A SAN+GF30%, General Purpose Feature: Injection Molding, SAN+GF30%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9 and 65997-17-3Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUPOS HR2207A ABS+GF20%, General Purpose, Heat Resistance Feature: Injection Molding, ABS+GF20%, General Purpose, Heat ResistanceApplication: Electric & Electronic (Housing, Components)Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | ASTM D638 |
| LG Chemical LUPOY GP-5300 General Purpose PC/ABS Alloy, 30% Polymer Alloy, High Strength, Dimensional Stability Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Greene Tweed Arlon® 1000 Polyketone Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® CS860 PBT+PET (Asia Pacific) 30% glass reinforced PBT+PET blend. Color stable, FR. Housewares, appliances; iron skirt, oven trim/panels.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Techmer ES HiFill® PA12 GF30 HS L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedInformati.. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Techmer ES HiFill® PA12 GF30 L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific) Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Techmer ES HiFill® PA6/6 GF/M36 HS BK 36% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 36% Filler by Weight and Mineral Filler, 36% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Techmer ES Luriblend® PA6/6 GF10 TL10 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(5%)Features: Lubricated, Good Wear Resistance, Low Fricti.. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | ASTM D638 |
| Techmer ES Luriblend® PC CF10 TL15 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: Lubricated and Flame RetardantAppearance: BlackInformation provided.. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® HN-3203G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® HN-3203G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NH-8310 MPPE, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL IGN320 PPE+PS 20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL NF1030 PPE+PS (Asia Pacific) |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® NH-8310 MPPE, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Cheng Yu Plastic ML3425 PC, 25% Glass Fiber |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Cheng Yu Plastic NG1200S Nylon 66, 20% Glass Fiber Reinforced |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | chs 2.0 in/min; ASTM D638 |
| Diamond Polymers DIAMALOY 1001 CF20 20% Carbon Fiber Filled ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Cheng Yu Plastic FR200GV20 Flame Retardant Nylon 66, 20% Glass Fiber |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | Dry; ASTM D638 |
| Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66 15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei |
|||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM 638 |
| PlastxWorld CEVIAN® B2506 30% GF PBT/ABS Alloy Glass fiber reinforced PBT/ABS alloy.Information provided by PlastxWorld Inc. |
|||
| Tensile Strength, Yield | 108 MPa | 15700 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL CN5246 PPE+PS (Asia Pacific) |
|||