- LG Chemical LUPOS GP2305A SAN+GF30%, General Purpose
LG Chemical LUPOS GP2305A SAN+GF30%, General Purpose
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS GP2305A SAN+GF30%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, SAN+GF30%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0020 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 152 MPa @Thickness 3.20 mm |
22000 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 8.83 GPa @Thickness 3.20 mm |
1280 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C @Thickness 6.40 mm |
217 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK) (Unverified Data**)
- Ineos T50-800-01 Polyethylene Copolymer
- Westlake MC2001 High Density Polyethylene Coating
- A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
- Arlon 55586XC028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- 3M 5640 Silicone Rubber Termination Kits
- DuPont Performance Polymers Zytel® 79G13HSL BK039 Nylon 66 (Unverified Data**)
- Solvay Specialty Polymers Veradel® 3600RP Polyethersulfone (PESU) (Unverified Data**)
- DSM Akulon® K225-KV PA6 FR(30)
Copyright © lookpolymers.com All Rights Reserved