LG Chemical LUPOS HR2207A ABS+GF20%, General Purpose, Heat Resistance
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS HR2207A ABS+GF20%, General Purpose, Heat Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, ABS+GF20%, General Purpose, Heat ResistanceApplication: Electric & Electronic (Housing, Components)Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 2.5 % @Thickness 3.20 mm |
2.5 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 142 MPa @Thickness 3.20 mm |
20600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 6.86 GPa @Thickness 3.20 mm |
996 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 6.40 mm |
225 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 235 °C | 428 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Nozzle Temperature | 230 - 245 °C | 446 - 473 °F | Injection Molding |
| Melt Temperature | 235 - 245 °C | 455 - 473 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B1 GF 15 FRX 5 PBT reinforced with 15% glass fibre, with flame retardant
- Michelman® Mold Release 225SS Synthetic wax emulsion
- SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK
- SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 (Europe-Africa-Middle East)
- Samsung Cheil Industries Starex® TF-0956 HI-PMMA
- Formosa Plastics Formolene® 4101N Staple Fiber and Injection Molding Polypropylene
- Teknor Apex Telcar® TL-8730R Thermoplastic Elastomer
- Cadi C17500 Copper Alloy
- BASF Ultramid® A27 E PA66
Copyright © lookpolymers.com All Rights Reserved