Greene Tweed Arlon® 1000 Polyketone
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Greene Tweed |
| Trade Name | Arlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Greene Tweed Arlon® 1000 Polyketone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprietary manufacturing and machining processes to ensure that Arlons properties consistently outperform the competition.Greene, Tweed offers several different Arlon materials, and all provide high tensile strength and elongation properties, excellent shear strength and creep resistance, outstanding fatigue resistance, broad chemical and radiation resistance, and no susceptibility to hydrolysis (steam/hot water). Our engineers work one on one with customers to find the right solution for each specific application.Information provided by Greene Tweed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Deformation | 0.090 % | 0.090 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 104 | 104 | ASTM D785 |
| Hardness, Shore D | 88 | 88 | ASTM D2240 |
| Tensile Strength at Break | 96.5 MPa | 14000 psi | ASTM D368 |
| 29.6 MPa @Temperature 316 °C |
4300 psi @Temperature 600 °F |
||
| Tensile Strength, Ultimate | 51.7 MPa @Temperature 149 °C |
7500 psi @Temperature 300 °F |
|
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Strength | 174 MPa | 25300 psi | ASTM D790 |
| 4.83 MPa @Temperature 316 °C |
700 psi @Temperature 600 °F |
||
| 72.4 MPa @Temperature 149 °C |
10500 psi @Temperature 300 °F |
||
| Flexural Modulus | 4.14 GPa | 600 ksi | Flexural 0.5% Secant Modulus; ASTM D790 |
| Compressive Strength | 131 MPa | 19000 psi | ASTM D695 |
| Shear Strength | 85.5 MPa | 12400 psi | Axial; ASTM D732 |
| 85.5 MPa | 12400 psi | Transverse; ASTM D732 | |
| 15.9 MPa @Temperature 316 °C |
2300 psi @Temperature 600 °F |
||
| 46.9 MPa @Temperature 149 °C |
6800 psi @Temperature 300 °F |
||
| Secant Modulus | 4.24 GPa | 615 ksi | Tensile 0.5% Secant Modulus; ASTM D638 |
| Coefficient of Friction, Dynamic | 0.29 | 0.29 | PV=12600 psi-fi./min.; ASTM G77 |
| K (wear) Factor | 105 x 10-8 mm³/N-M | 52.0 x 10-10 in³-min/ft-lb-hr | ASTM G77 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 46.8 µm/m-°C @Temperature <=149 °C |
26.0 µin/in-°F @Temperature <=300 °F |
ASTM E228 |
| 135 µm/m-°C @Temperature >=149 °C |
75.0 µin/in-°F @Temperature >=300 °F |
ASTM E228 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Tan |
Users viewing this material also viewed the following:
- Quantum Composites QC-7810 55% Glass Fiber Polyester SMC (discontinued **)
- Iran Petrochemical (PCC) LL0220KJ Linear Low Density Polyethylene
- Kraton® D1102 A (SBS) Liner Block Copolymer
- SABIC Innovative Plastics Valox® 815F PBT+PET (Asia Pacific)
- Excalibar ExBar™ W 325 Barite BaSO4 Powder
- Ensinger Tecatron® XP-84 Compression Molded PPS Compound, 30% Graphite Filled
- Fainplast Compounds CL 83 Flexible PVC, Sheathing
- Braskem GM7040G HDPE High Density Extrusion Polyethylene
- Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
- ACC QSil 553 QSI Quantum Silicones Silicone Potting Material
Copyright © lookpolymers.com All Rights Reserved