SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.24 GPa | 1050 ksi | 1 mm/min; ISO 527 |
| 7.65 GPa | 1110 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 149 MPa | 21600 psi | ISO 178 |
| 153 MPa | 22200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 149 MPa | 21600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.53 GPa | 947 ksi | 2 mm/min; ISO 178 |
| 7.03 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.58 J/cm | 10.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
- LyondellBasell Sequel® 1718 Engineered Polyolefin
- Mitsubishi Hostaphan® RN, 100 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Johnson Matthey SW 850 Platinum w/ 15% Iridium Jewelry Alloy
- A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy
- Unipetrol PE HD LITEN® MB/ML 73 HDPE
- ExxonMobil Bicor® 120 SLP OPP Film
- Arlon T2040-B004 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber
- DSM Arnite® T08 200 (extrusion) T08 200 PBT (European and Asian Grade) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved