SABIC Innovative Plastics Valox® CS860 PBT+PET (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® CS860 PBT+PET (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass reinforced PBT+PET blend. Color stable, FR. Housewares, appliances; iron skirt, oven trim/panels.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 45 g/10 min @Load 5.00 kg, Temperature 266 °C |
45 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 6.20 GPa | 899 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 155 MPa | 22500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Temperature 23.0 °C |
10.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C @Thickness 6.40 mm |
369 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.760 mm |
V-0 @Thickness 0.0299 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC code 3; UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | PLC code 0; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C2800 PC+ABS (Asia Pacific)
- H.C. Starck Amperit® 140.3 Tungsten (W)
- SABIC Innovative Plastics ULTEM 2400 PEI (Asia Pacific)
- Silberline Silvex® 420-15-D
- Teknor Apex Uniprene® UN-1069E2 Thermoplastic Vulcanizate
- Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- Braskem LH218 Cast Film Extrusion Linear Low Density Polyethylene
- 3M Scotch-Weld™ 5 Neoprene Contact Adhesive
- Teknor Apex Sarlink® 3140 Thermoplastic Elastomer
- American Polymers API 645-21 Polystyrene
Copyright © lookpolymers.com All Rights Reserved