SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.19 % | 0.19 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 250 °C |
40 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 27 g/10 min @Load 5.00 kg, Temperature 220 °C |
27 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 27 g/10 min @Load 5.00 kg, Temperature 250 °C |
27 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| 119 MPa | 17300 psi | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| 8.0 % | 8.0 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Elongation at Yield | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1 mm/min; ISO 527 |
| 11.1 GPa | 1610 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 180 MPa | 26100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 8.97 GPa | 1300 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.18 GPa | 1330 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.920 J/cm | 1.72 ft-lb/in | ASTM D256 |
| 0.750 J/cm @Temperature -30.0 °C |
1.41 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 7.94 J/cm | 14.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 20.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 102 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 102 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 157 °C | 315 °F | Rate B/50; ASTM D1525 |
| 157 °C | 315 °F | Rate B/50; ISO 306 | |
| 157 °C | 315 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 by SABIC-IP |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- MV Labs ZR1000 ZrO2 Zirconium(IV) oxide (low Hf)
- Precision Polymer Engineering Z95X Hydrogenated NBR Compound
- ExxonMobil Escorene® LD-720 High EVA Film Resin (discontinued **)
- SABIC Innovative Plastics LNP COLORCOMP DX99340H PC
- Flint Hills P4G2Z-159 Polypropylene Homopolymer
- Lucas-Milhaupt BRAZE 505 Carbide Brazing Alloy
- A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene
- Hexcel® HexWeb® HRH-36® Flex-Core® HRH-36 - F50 - 3.5 Aramid Honeycomb
- Arlon 51191R014 0.015" Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved