Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 135 MPa | 19600 psi | |
Plastcom SLOVAMID 66 GF 20 PA66, 20% glass fibre FeaturesChemically reinforced with 20 % glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. .. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 66 GF 25 FRI 3 Polyamide 66, 25% Glass Fiber, Halogen Free Flame Retardant FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fiber and non-halogen flame retardant, with heat and flammability resistance, achieves V-0 in accordance with UL 94. Non-h.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID® 6 GF 25 FRC 4 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 25 % glass fiber, flame retarded with halogen free flame retardant. Main features: flammability according to UL 94 3 at 1,6mm, glow wire at 960°C. Applic.. |
|||
Tensile Strength at Break | <= 135 MPa | <= 19600 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A12^ QF2515 Nylon 66,Mineral and Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | |
Plastcom SLOVAMID 6 GF 25 FRA 5 LS PA6, 25% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 25% glass fibre, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°C,.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-1/-2 |
DSM Akulon® S223-PG6U (Dry) 33% Glass Reinforced, Impact Modified Nylon 66 (North America)
(discontinued **)& Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | |
Idemitsu Kosan Xarec® WA 550 SPS, 30% Glass Filled Crystalline Polymer, Glass Filled. Used in Automotive and Industrial applications |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® AKV 35 H3.0 000000 Nylon 66, 35% Glass Fiber PA 66, injection molding grade, 35% glass fibers, good heat-ageing resistance |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-1/-2 |
Lanxess Durethan® DP 1441/40 H2.0 EF 900116 Nylon 6, 40% Glass Fiber + Mineral PA 6, injection molding grade, 40% glass fibers/mineral, good heat-ageing resistance, good surface, good flowability (Easy Flow), low warpage |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® ECO PA GF30 909040 Nylon 6, 30% Glass Fiber PA 6 (mainly), 30% glass fibers, injection molding, contains at least 80% pre-consumer recycled material, properties may change considerably from lot to lotInformation provided by LANXESS. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66 LNP* LUBRICOMP* RFP36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 V30 PA66, 30% glass fiber, Conditioned Description: TECHNYL® A 218 V30 is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The .. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® V8280SF PBT+PET High Modulus, PBT+PET, 40% Glass Reinforced, Mold Release, Super High Flow |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-93 |
Wellman Wellamid® GF25-60 XE-NBK1 25% Glass Fiber Reinforced Nylon 6 Description: Glass Fiber Reinforced Nylon 6Information provided by Wellman. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-93 |
Wellman Wellamid® MRGF25/25 22H-GY1 Nylon 66, 25% Mineral and 25% Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-93 |
Wellman Wellamid® MRGF25/25 22H-NBK1 Nylon 66, 25% Mineral and 25% Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-50H FWA black 9225 PA12-GF50 Product description: Grilamid LV-50H FWA black 9225 is a 50 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6
(Unverified Data**) 15% Glass Reinforced Polyamide 6Zytel 73G15L NC010 is a 15% glass fiber reinforced polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
Eurotec® Tecomid® NB40 GR30 NL IM PA6, 30% glass fiber reinforced, impact modified, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
BASF Ultramid® 66 H2 G/25-V0KB1 BK 3324 PA66 (Dry) Description: Ultramid 66 H2 G/25-V0KB1 BK3324 is a 25% glass reinforced, heat stabilized injection molding grade. It's a V-0 self-extinguishing, with phosphorous. It offers good flowability, surface.. |
|||
Tensile Strength at Break | 135 MPa @Temperature -40.0 °C |
19600 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Strength at Break | 135 MPa @Temperature -40.0 °C |
19600 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Strength at Break | 135 MPa @Temperature 60.0 °C |
19600 psi @Temperature 140 °F |
|
BASF Ultrason E 2010 G6 30% Glass Filled PES Ultrason E 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PES grade with high rigidity and strength. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-1/-2 |
DuPont Performance Polymers Rynite® FR530L NC010 Polyethylene Terephthalate (PET) Rynite FR530 NC010 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 216 V30 Natural FA PA66, 30% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 30% of glass fiber and modified for enhanced injection molding.Available in: Europe Product Applications: This material offers an excellent combination b.. |