- Lanxess Durethan® ECO PA GF30 909040 Nylon 6, 30% Glass Fiber
Lanxess Durethan® ECO PA GF30 909040 Nylon 6, 30% Glass Fiber
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® ECO PA GF30 909040 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6 (mainly), 30% glass fibers, injection molding, contains at least 80% pre-consumer recycled material, properties may change considerably from lot to lotInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 2.5 % | 2.5 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 8.50 GPa | 1230 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 210 MPa @Strain 3.00 % |
30500 psi @Strain 3.00 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 7.50 GPa | 1090 ksi | d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | d.a.m.; ISO 179-1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | >= 210 °C | >= 410 °F | 10°C/min; ISO 11357-1, -3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6/XX, GR, 14-080, GF30 |
Users viewing this material also viewed the following:
- Pacific Sintered Materials F-244-S(HT) High Carbon Steel Powdered Metal
- Polykemi AB POLYfill PP EIP16020 F PP Mineral Reinforced, Extrusion Grade, Low CLTE
- Silberline Sparkle Silver® 6246-AR
- A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
- Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene
- 3M Scotch® 375 Superior Performance Box Sealing Tape
- ATI Allegheny Ludlum A6 Tool Steel, UNS T30106
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 440A, Hardened + 649°C (1200°F) Temper
- BASF Ultramid® B3WG5 BK 00564 25% Glass Filled PA6 (Conditioned)