BASF Ultrason E 2010 G6 30% Glass Filled PES

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled
Manufacturer BASF
Trade Name Ultrason E
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason E 2010 G6 30% Glass Filled PES.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Ultrason E 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PES grade with high rigidity and strength.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
Water Absorption 1.6 %
1.6 %
ISO 62
Moisture Absorption at Equilibrium 0.60 %
0.60 %
23°C/50% R.H.; ISO 62
Viscosity Test 56 cm³/g
56 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0028 cm/cm
0.0028 in/in
ISO 294
Linear Mold Shrinkage, Transverse 0.0058 cm/cm
0.0058 in/in
ISO 294
Melt Flow 25 g/10 min

@Load 10.0 kg,
Temperature 360 °C
 25 g/10 min

@Load 22.0 lb,
Temperature 680 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 224 MPa
32500 psi
ISO 2039-1
Tensile Strength at Break 140 MPa
20300 psi
5mm/min; ISO 527-2
100 MPa

@Temperature 140 °C
 14500 psi

@Temperature 284 °F
125 MPa

@Temperature 100 °C
 18100 psi

@Temperature 212 °F
135 MPa

@Temperature 60.0 °C
 19600 psi

@Temperature 140 °F
150 MPa

@Temperature 20.0 °C
 21800 psi

@Temperature 68.0 °F
Tensile Stress 31.0 MPa

@# of Cycles 1.00e+7 ,
Temperature 180 °C
 4500 psi

@# of Cycles 1.00e+7 ,
Temperature 356 °F
38.0 MPa

@# of Cycles 1.00e+6 ,
Temperature 180 °C
 5510 psi

@# of Cycles 1.00e+6 ,
Temperature 356 °F
43.0 MPa

@# of Cycles 100000 ,
Temperature 180 °C
 6240 psi

@# of Cycles 100000 ,
Temperature 356 °F
50.0 MPa

@Strain 0.600 %,
Temperature 160 °C
 7250 psi

@Strain 0.600 %,
Temperature 320 °F
 ISO 527
50.0 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 7250 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 527
75.0 MPa

@Strain 1.00 %,
Temperature 160 °C
 10900 psi

@Strain 1.00 %,
Temperature 320 °F
 ISO 527
80.0 MPa

@Strain 1.40 %,
Temperature 160 °C
 11600 psi

@Strain 1.40 %,
Temperature 320 °F
 ISO 527
80.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 11600 psi

@Strain 1.00 %,
Temperature 73.4 °F
 ISO 527
125 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 18100 psi

@Strain 1.50 %,
Temperature 73.4 °F
 ISO 527
Tensile Strength, Yield 140 MPa
20300 psi
50mm/min; ISO 527-2
Elongation at Break 1.9 %
1.9 %
5mm/min; ISO 527-2
Elongation at Yield 1.9 %
1.9 %
50mm/min; ISO 527-2
0.189 %

@Time 3600 sec,
Pressure 15.0 MPa
 0.189 %

@Time 1.00 hour,
Pressure 2180 psi
 ISO 899
0.19 %

@Pressure 15.0 MPa,
Time 360000 sec
 0.19 %

@Pressure 2180 psi,
Time 100 hour
 ISO 899
0.20 %

@Pressure 15.0 MPa,
Time 3.60e+7 sec
 0.20 %

@Pressure 2180 psi,
Time 10000 hour
 ISO 899
0.20 %

@Pressure 10.0 MPa,
Time 360000 sec
 0.20 %

@Pressure 1450 psi,
Time 100 hour
 180°C; ISO 899
0.20 %

@Time 3600 sec,
Pressure 10.0 MPa
 0.20 %

@Time 1.00 hour,
Pressure 1450 psi
 180°C; ISO 899
0.25 %

@Pressure 10.0 MPa,
Time 3.60e+7 sec
 0.25 %

@Pressure 1450 psi,
Time 10000 hour
 180°C; ISO 899
0.30 %

@Time 3600 sec,
Pressure 20.0 MPa
 0.30 %

@Time 1.00 hour,
Pressure 2900 psi
 180°C; ISO 899
0.30 %

@Pressure 20.0 MPa,
Time 360000 sec
 0.30 %

@Pressure 2900 psi,
Time 100 hour
 180°C; ISO 899
0.30 %

@Time 3600 sec,
Pressure 30.0 MPa
 0.30 %

@Time 1.00 hour,
Pressure 4350 psi
 180°C; ISO 899
0.35 %

@Time 3600 sec,
Pressure 30.0 MPa
 0.35 %

@Time 1.00 hour,
Pressure 4350 psi
 180°C; ISO 899
0.38 %

@Pressure 30.0 MPa,
Time 360000 sec
 0.38 %

@Pressure 4350 psi,
Time 100 hour
 180°C; ISO 899
0.40 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
 0.40 %

@Pressure 4350 psi,
Time 10000 hour
 ISO 899
0.40 %

@Time 3600 sec,
Pressure 40.0 MPa
 0.40 %

@Time 1.00 hour,
Pressure 5800 psi
 180°C; ISO 899
0.40 %

@Pressure 20.0 MPa,
Time 3.60e+7 sec
 0.40 %

@Pressure 2900 psi,
Time 10000 hour
 180°C; ISO 899
0.40 %

@Pressure 30.0 MPa,
Time 360000 sec
 0.40 %

@Pressure 4350 psi,
Time 100 hour
 ISO 899
0.50 %

@Pressure 40.0 MPa,
Time 360000 sec
 0.50 %

@Pressure 5800 psi,
Time 100 hour
 ISO 899
0.50 %

@Time 3600 sec,
Pressure 50.0 MPa
 0.50 %

@Time 1.00 hour,
Pressure 7250 psi
 180°C; ISO 899
0.55 %

@Time 3600 sec,
Pressure 45.0 MPa
 0.55 %

@Time 1.00 hour,
Pressure 6530 psi
 ISO 899
0.60 %

@Pressure 45.0 MPa,
Time 360000 sec
 0.60 %

@Pressure 6530 psi,
Time 100 hour
 ISO 899
0.78 %

@Time 3600 sec,
Pressure 60.0 MPa
 0.78 %

@Time 1.00 hour,
Pressure 8700 psi
 ISO 899
0.80 %

@Pressure 60.0 MPa,
Time 360000 sec
 0.80 %

@Pressure 8700 psi,
Time 100 hour
 ISO 899
0.80 %

@Pressure 50.0 MPa,
Time 360000 sec
 0.80 %

@Pressure 7250 psi,
Time 100 hour
 180°C; ISO 899
0.90 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
 0.90 %

@Pressure 4350 psi,
Time 10000 hour
 ISO 899
0.90 %

@Pressure 60.0 MPa,
Time 3.60e+7 sec
 0.90 %

@Pressure 8700 psi,
Time 10000 hour
 ISO 899
0.99 %

@Time 3600 sec,
Pressure 75.0 MPa
 0.99 %

@Time 1.00 hour,
Pressure 10900 psi
 ISO 899
1.1 %

@Pressure 75.0 MPa,
Time 360000 sec
 1.1 %

@Pressure 10900 psi,
Time 100 hour
 ISO 899
1.23 %

@Pressure 75.0 MPa,
Time 3.60e+7 sec
 1.23 %

@Pressure 10900 psi,
Time 10000 hour
 ISO 899
1.5 %

@Pressure 40.0 MPa,
Time 3.60e+7 sec
 1.5 %

@Pressure 5800 psi,
Time 10000 hour
 180°C; ISO 899
2.5 %

@Pressure 50.0 MPa,
Time 3.60e+7 sec
 2.5 %

@Pressure 7250 psi,
Time 10000 hour
 180°C; ISO 899
6.1 %

@Pressure 45.0 MPa,
Time 3.60e+7 sec
 6.1 %

@Pressure 6530 psi,
Time 10000 hour
 ISO 899
Creep Strength 22.0 MPa

@Time 3.60e+7 sec
 3190 psi

@Time 10000 hour
 in water at 95°C
30.0 MPa

@Time 3.60e+6 sec
 4350 psi

@Time 1000 hour
 in water at 95°C
41.0 MPa

@Time 360000 sec
 5950 psi

@Time 100 hour
 in water at 95°C
55.0 MPa

@Time 36000 sec
 7980 psi

@Time 10.0 hour
 in water at 95°C
Modulus of Elasticity 9.80 GPa

@Temperature 160 °C
 1420 ksi

@Temperature 320 °F
 ISO 527
9.85 GPa

@Temperature 60.0 °C
 1430 ksi

@Temperature 140 °F
 ISO 527
9.90 GPa

@Temperature 20.0 °C
 1440 ksi

@Temperature 68.0 °F
 ISO 527
10.0 GPa

@Temperature 120 °C
 1450 ksi

@Temperature 248 °F
 ISO 527
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527-2
Fatigue Strength 43.0 MPa

@# of Cycles 1.00e+7
6240 psi

@# of Cycles 1.00e+7
52.0 MPa

@# of Cycles 1.00e+6
7540 psi

@# of Cycles 1.00e+6
65.0 MPa

@# of Cycles 100000
9430 psi

@# of Cycles 100000
Shear Modulus 0.200 GPa

@Temperature 225 °C
 29.0 ksi

@Temperature 437 °F
 ISO 6721
0.900 GPa

@Temperature 200 °C
 131 ksi

@Temperature 392 °F
 ISO 6721
0.950 GPa

@Temperature 100 °C
 138 ksi

@Temperature 212 °F
 ISO 6721
1.00 GPa

@Temperature 50.0 °C
 145 ksi

@Temperature 122 °F
 ISO 6721
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/A
Izod Impact, Unnotched (ISO) 42.0 kJ/m²

@Temperature 120 °C
 20.0 ft-lb/in²

@Temperature 248 °F
 ISO 179/1eU
50.0 kJ/m²

@Temperature 25.0 °C
 23.8 ft-lb/in²

@Temperature 77.0 °F
 ISO 179/1eU
57.0 kJ/m²

@Temperature -25.0 °C
 27.1 ft-lb/in²

@Temperature -13.0 °F
 ISO 179/1eU
59.0 kJ/m²

@Temperature 0.000 °C
 28.1 ft-lb/in²

@Temperature 32.0 °F
 ISO 179/1eU